LIGHTNING CLEAR

Posted on July 16, 2013 by Adam Robertson

High gloss clear with a Gold sparkle

MC1044 LIGHTNING CLEAR
CHEMISTRY POLYESTER TGIC A
REGULAR CURE SCHEDULE 375F / 15 MIN
MIN RANGE 356F / 25 MIN
MAX RANGE 400F / 10 MIN
RECOMMENDED THICKNESS 2.5-3.5 mils
PENCIL HARDNESS 2H minimum
SPECIFIC GRAVITY 1.2-1.8 g/cm3
THEORETICAL COVERAGE 51.5 ft2 /lb at 2.5 mils
PENCIL HARDNESS 2H minimum
GLOSS LEVEL (60°) 80-95+
SALT SPRAY 1,000 hours
BALL IMPACT 80 in/lb
SDS Sheet info # #6A – Polyester TGIC (Group A)
SDS link https://emeraldcoatings.com/sds-sheets/
WEATHER RESISTANT POWDER COATING FOR INTERIOR AND EXTERIOR APPLICATIONS.   When coating in 2-3 stages, always particularly cure the base coat around 50-75% of the recommended cure schedule to allow the top coat to properly cross-link with the base coat. This method of curing will result in the best possible bond between coats. over curing the base coat can cause possible Delamination between coatings.

 

 

 

Comments Off on LIGHTNING CLEAR

HD BLACK CHERRY

Posted on July 16, 2013 by Adam Robertson
MC1005 HD BLACK CHERRY
CHEMISTRY Polyester TGIC Metallic
REGULAR CURE TEMP 15 Minutes@ 375°F
MIN TEMP NA
MAX TEMP NA
RECOMMENDED THICKNESS 1.5 TO 3.5 MILS
PENCIL HARDNESS 2H
SPECIFIC GRAVITY 1.26 +/- .05
THEORETICAL COVERAGE 56 sq/ft @ 2.0 mils
PENCIL HARDNESS 2H minimum
GLOSS LEVEL (60°) 85-95+
SALT SPRAY 1,000 hours
BALL IMPACT 80 in/lb
SDS Sheet info # #9 – Polyester TGIC Metallic
SDS link https://emeraldcoatings.com/sds-sheets/
*Clear Coat Recommended, will Improved Mar Resistance and will improve the over all look and depth of the metallic finish.  *When coating in 2-3 stages, always particularly cure the base coat around 50-75% of the recommended cure schedule to allow the top coat to properly cross-link with the base coat. This method of curing will result in the best possible bond between coats. Over curing the base coat can cause possible delamination between coatings.
Comments Off on HD BLACK CHERRY

BROWN ORANGE GLOW

Posted on July 16, 2013 by Adam Robertson
MC1016 BROWN ORANGE GLOW
CHEMISTRY Polyester TGIC Metallic
REGULAR CURE TEMP 375F/10 MIN
MIN TEMP 350F/15 MIN
MAX TEMP 400F/7 MIN
RECOMMENDED THICKNESS 2.0 TO 3.0 MILS
PENCIL HARDNESS 2H
SPECIFIC GRAVITY 1.44 +/- .05
THEORETICAL COVERAGE 67 sq/ft @ 2.0 mils
PENCIL HARDNESS 2H minimum
GLOSS LEVEL (60°) 80-95+
SALT SPRAY 1,008 hrs
BALL IMPACT 100 in/lb
SDS Sheet info # #9 – Polyester TGIC Metallic
SDS link https://emeraldcoatings.com/sds-sheets/
*Clear Coat Recommended, will Improved Mar Resistance and will improve the over all look and depth of the metallic finish.  *When coating in 2-3 stages, always particularly cure the base coat around 50-75% of the recommended cure schedule to allow the top coat to properly cross-link with the base coat. This method of curing will result in the best possible bond between coats. Over curing the base coat can cause possible delamination between coatings.
Comments Off on BROWN ORANGE GLOW

CHARCOAL PEARL METALLIC

Posted on July 16, 2013 by Adam Robertson

CHARCOAL PEARL METALLIC

MC1019 CHARCOAL PEARL METALLIC
CHEMISTRY Polyester TGIC Metallic
REGULAR CURE TEMP 375F/10 MIN
MIN TEMP 350F/15 MIN
MAX TEMP 400F/7 MIN
RECOMMENDED THICKNESS 2.0 TO 3.0 MILS
PENCIL HARDNESS 2H
SPECIFIC GRAVITY 1.43 +/- .05
THEORETICAL COVERAGE 68 sq/ft @ 2.0 mils
PENCIL HARDNESS 2H minimum
GLOSS LEVEL (60°) 80-95+
SALT SPRAY n/a
BALL IMPACT 120 in/lb
SDS Sheet info # #9 – Polyester TGIC Metallic
SDS link https://emeraldcoatings.com/sds-sheets/
*Clear Coat Recommended, will Improved Mar Resistance and will improve the over all look and depth of the metallic finish.  *When coating in 2-3 stages, always particularly cure the base coat around 50-75% of the recommended cure schedule to allow the top coat to properly cross-link with the base coat. This method of curing will result in the best possible bond between coats. Over curing the base coat can cause possible delamination between coatings.
Comments Off on CHARCOAL PEARL METALLIC

SATIN BLACK PEARL

Posted on July 16, 2013 by Adam Robertson
CHEMISTRY SATIN BLACK PEARL
CHEMISTRY Polyester TGIC Metallic
REGULAR CURE TEMP 375F/15 MIN
MIN TEMP NA
MAX TEMP NA
RECOMMENDED THICKNESS 2.0-3.0 mils
PENCIL HARDNESS 4H minimum
SPECIFIC GRAVITY 1.67 +/-0.05 g/cm³
THEORETICAL COVERAGE 115.14 sq.ft/lb/mil
PENCIL HARDNESS 2H minimum
GLOSS LEVEL (60°) 30-40
SALT SPRAY 2,500 hours
BALL IMPACT 80 in/lb
SDS Sheet info # #9 – Polyester TGIC Metallic
SDS link https://emeraldcoatings.com/sds-sheets/
No top coat will leave you with a unique satin metallic finish. Add a high gloss clear to make the metallic’s pop and turn this into a whole different colour.  Add a flat clear to keep the satin look while adding extra protection to the part.   This product is exterior durable however, parts subject to more extreme conditions like car rims should be clear coated. When coating in 2-3 stages, always particularly cure the base coat around 50-75% of the recommended cure schedule to allow the top coat to properly cross-link with the base coat. This method of curing will result in the best possible bond between coats. over curing the base coat can cause possible De-lamination between coatings.
Comments Off on SATIN BLACK PEARL

HUNTER GREEN METALLIC

Posted on July 16, 2013 by Adam Robertson
MC1041 HUNTER GREEN METALLIC
CHEMISTRY Polyester TGIC Metallic
REGULAR CURE TEMP 15 Minutes@ 375°F
MIN TEMP NA
MAX TEMP NA
RECOMMENDED THICKNESS 1.5 TO 3.5 MILS
PENCIL HARDNESS 2H
SPECIFIC GRAVITY 1.26 +/- .05
THEORETICAL COVERAGE 56 sq/ft @ 2.0 mils
PENCIL HARDNESS 2H minimum
GLOSS LEVEL (60°) 85-95+
SALT SPRAY 1,000 hours
BALL IMPACT 80 in/lb
SDS Sheet info # #9 – Polyester TGIC Metallic
SDS link https://emeraldcoatings.com/sds-sheets/
*Clear Coat Recommended, will Improved Mar Resistance and will improve the over all look and depth of the metallic finish.  *When coating in 2-3 stages, always particularly cure the base coat around 50-75% of the recommended cure schedule to allow the top coat to properly cross-link with the base coat. This method of curing will result in the best possible bond between coats. Over curing the base coat can cause possible delamination between coatings.
Comments Off on HUNTER GREEN METALLIC

SUBLIME TWIST

Posted on July 16, 2013 by Adam Robertson
MC1074 SUBLIME TWIST
CHEMISTRY Polyester TGIC Metallic
REGULAR CURE TEMP 375F/10 MIN
MIN TEMP 350F/15 MIN
MAX TEMP 400F/7 MIN
RECOMMENDED THICKNESS 2.0 TO 3.0 MILS
PENCIL HARDNESS 2H
SPECIFIC GRAVITY 1.43 +/- .05
THEORETICAL COVERAGE 68 sq/ft @ 2.0 mils
PENCIL HARDNESS 2H minimum
GLOSS LEVEL (60°) 80-95+
SALT SPRAY n/a
BALL IMPACT 120 in/lb
SDS Sheet info # #9 – Polyester TGIC Metallic
SDS link https://emeraldcoatings.com/sds-sheets/
*Clear Coat Recommended, will Improved Mar Resistance and will improve the over all look and depth of the metallic finish.  *When coating in 2-3 stages, always particularly cure the base coat around 50-75% of the recommended cure schedule to allow the top coat to properly cross-link with the base coat. This method of curing will result in the best possible bond between coats. Over curing the base coat can cause possible delamination between coatings.

 

 

Comments Off on SUBLIME TWIST

MAHOGANY METALLIC

Posted on July 16, 2013 by Adam Robertson
CHEMISTRY MAHOGANY METALLIC
CHEMISTRY POLYURETHANE Metallic
REGULAR CURE TEMP 15 Minutes@ 375°F
MIN TEMP NA
MAX TEMP NA
RECOMMENDED THICKNESS 1.5 TO 3.5 MILS
PENCIL HARDNESS 2H
SPECIFIC GRAVITY 1.26 +/- .05
THEORETICAL COVERAGE 56 sq/ft @ 2.0 mils
PENCIL HARDNESS 2H minimum
GLOSS LEVEL (60°) 85-95+
SALT SPRAY 1,000 hours
BALL IMPACT 80 in/lb
SDS Sheet info # #8 – Polyurethane Metallic
SDS link https://emeraldcoatings.com/sds-sheets/
*Clear Coat Recommended, will Improved Mar Resistance and will improve the over all look and depth of the metallic finish.  *When coating in 2-3 stages, always particularly cure the base coat around 50-75% of the recommended cure schedule to allow the top coat to properly cross-link with the base coat. This method of curing will result in the best possible bond between coats. Over curing the base coat can cause possible delamination between coatings.

 

 

Comments Off on MAHOGANY METALLIC

BLUE ICE TEMPEST EXPLOSION

Posted on July 16, 2013 by Adam Robertson
MC1010 BLUE ICE TEMPEST EXPLOSION
CHEMISTRY Polyester TGIC Metallic
REGULAR CURE TEMP 15 Minutes@ 375°F
MIN TEMP NA
MAX TEMP NA
RECOMMENDED THICKNESS 1.5 TO 3.5 MILS
PENCIL HARDNESS 2H
SPECIFIC GRAVITY 1.26 +/- .05
THEORETICAL COVERAGE 56 sq/ft @ 2.0 mils
PENCIL HARDNESS 2H minimum
GLOSS LEVEL (60°) 85-95+
SALT SPRAY 1,000 hours
BALL IMPACT 80 in/lb
SDS Sheet info # #9 – Polyester TGIC Metallic
SDS link https://emeraldcoatings.com/sds-sheets/
*Clear Coat Recommended, will Improved Mar Resistance and will improve the over all look and depth of the metallic finish.  *When coating in 2-3 stages, always particularly cure the base coat around 50-75% of the recommended cure schedule to allow the top coat to properly cross-link with the base coat. This method of curing will result in the best possible bond between coats. Over curing the base coat can cause possible delamination between coatings.
Comments Off on BLUE ICE TEMPEST EXPLOSION

BLACK BRONZE ILLUSION

Posted on July 16, 2013 by Adam Robertson

BLACK BRONZE ILLUSION~ UNDER INDOOR LIGHT THE FINISH IS BLACK/BRONZE WITH A GOLD PEARL – PUT THE PRODUCT IN THE SUNLIGHT AND THE ILLUSION BEGINS !

 

MC1004 Black Bronze illusion
CHEMISTRY Polyester TGIC Metallic
REGULAR CURE TEMP 15 Minutes@ 375°F
MIN TEMP NA
MAX TEMP NA
RECOMMENDED THICKNESS 1.5 TO 3.5 MILS
PENCIL HARDNESS 2H
SPECIFIC GRAVITY 1.26 +/- .05
THEORETICAL COVERAGE 56 sq/ft @ 2.0 mils
PENCIL HARDNESS 2H minimum
GLOSS LEVEL (60°) 85-95+
SALT SPRAY 1,000 hours
BALL IMPACT 80 in/lb
SDS Sheet info # #9 – Polyester TGIC Metallic
SDS link https://emeraldcoatings.com/sds-sheets/
*Clear Coat Recommended, will Improved Mar Resistance and will improve the over all look and depth of the metallic finish.  *When coating in 2-3 stages, always particularly cure the base coat around 50-75% of the recommended cure schedule to allow the top coat to properly cross-link with the base coat. This method of curing will result in the best possible bond between coats. Over curing the base coat can cause possible delamination between coatings.
Comments Off on BLACK BRONZE ILLUSION

GRANET PEARL

Posted on July 16, 2013 by Adam Robertson
MC1033 GRANET PEARL
CHEMISTRY Polyester TGIC Metallic
REGULAR CURE TEMP 15 Minutes@ 375°F
MIN TEMP NA
MAX TEMP NA
RECOMMENDED THICKNESS 1.5 TO 3.5 MILS
PENCIL HARDNESS 2H
SPECIFIC GRAVITY 1.26 +/- .05
THEORETICAL COVERAGE 56 sq/ft @ 2.0 mils
PENCIL HARDNESS 2H minimum
GLOSS LEVEL (60°) 85-95+
SALT SPRAY 1,000 hours
BALL IMPACT 80 in/lb
SDS Sheet info # #9 – Polyester TGIC Metallic
SDS link https://emeraldcoatings.com/sds-sheets/
*Clear Coat Recommended, will Improved Mar Resistance and will improve the over all look and depth of the metallic finish.  *When coating in 2-3 stages, always particularly cure the base coat around 50-75% of the recommended cure schedule to allow the top coat to properly cross-link with the base coat. This method of curing will result in the best possible bond between coats. Over curing the base coat can cause possible delamination between coatings.
Comments Off on GRANET PEARL

SHATTERED BLUE

Posted on July 16, 2013 by Adam Robertson

SHATTERED BLUE POLYESTER POWDER    • GLOSS LEVEL = 80 -90% ON 60 DEGREE METER  • CURE SCHEDULE = 400F/10 MIN or 375/15min @ PMT  HARDNESS= H-2H IMPACT RESISTANCE: UP TO 80 IN/LB • RECOMMENDED MIL THICKNESS = 1.50 – 3.50 MILS  CROSS HATCH: 100%

*** CLEAR COAT NEEDED. EMERALD COATINGS RECOMMENDS A CLEAR FOR PROLONGED EXTERIOR USE AND IMPROVED MAR RESISTANCE.

Comments Off on SHATTERED BLUE

CHOCOLATE MAPLE METALLIC

Posted on July 16, 2013 by Adam Robertson
MC1020 CHOCOLATE MAPLE METALLIC
CHEMISTRY Polyester TGIC Metallic
REGULAR CURE TEMP 375F/10 MIN
MIN TEMP 350F/15 MIN
MAX TEMP 400F/7 MIN
RECOMMENDED THICKNESS 2.0 TO 3.0 MILS
PENCIL HARDNESS 2H
SPECIFIC GRAVITY 1.42 +/- .05
THEORETICAL COVERAGE 68 sq/ft @ 2 mils
PENCIL HARDNESS 2H minimum
GLOSS LEVEL (60°) 80-95+
SALT SPRAY n/a
BALL IMPACT 120 in/lb
SDS Sheet info # #9 – Polyester TGIC Metallic
SDS link https://emeraldcoatings.com/sds-sheets/
*Clear Coat Recommended, will Improved Mar Resistance and will improve the over all look and depth of the metallic finish.  *When coating in 2-3 stages, always particularly cure the base coat around 50-75% of the recommended cure schedule to allow the top coat to properly cross-link with the base coat. This method of curing will result in the best possible bond between coats. Over curing the base coat can cause possible delamination between coatings.

 

Comments Off on CHOCOLATE MAPLE METALLIC

PASSIONATE PINK

Posted on July 16, 2013 by Adam Robertson
CHEMISTRY PASSIONATE PINK
CHEMISTRY Polyester TGIC Metallic
REGULAR CURE TEMP 375F/10 MIN
MIN TEMP 350F/15 MIN
MAX TEMP 400F/7 MIN
RECOMMENDED THICKNESS 2.5-4 mils
PENCIL HARDNESS 2H
SPECIFIC GRAVITY 1.41 +/- .05
THEORETICAL COVERAGE 55 sq/ft @ 2.5 mils
PENCIL HARDNESS 2H minimum
GLOSS LEVEL (60°) 80-95+
SALT SPRAY 1,000 hours
BALL IMPACT 120 in/lb
SDS Sheet info # #9 – Polyester TGIC Metallic
SDS link https://emeraldcoatings.com/sds-sheets/
*Clear Coat Recommended, will Improved Mar Resistance and will improve the over all look and depth of the metallic finish.  *When coating in 2-3 stages, always particularly cure the base coat around 50-75% of the recommended cure schedule to allow the top coat to properly cross-link with the base coat. This method of curing will result in the best possible bond between coats. Over curing the base coat can cause possible delamination between coatings.
Comments Off on PASSIONATE PINK

FLAME RED COPPER BLAST

Posted on July 16, 2013 by Adam Robertson
MC1030 FLAME RED COPPER BLAST
CHEMISTRY Polyester TGIC Metallic
REGULAR CURE TEMP 400F/10 MIN @ PART METAL TEMPERATURE
MIN TEMP NA
MAX TEMP NA
RECOMMENDED THICKNESS 2.5-3.5 mils
PENCIL HARDNESS 2H minimum
SPECIFIC GRAVITY 1.2-1.8 g/cm3
THEORETICAL COVERAGE 51.5 ft2 /lb at 2.5 mils
PENCIL HARDNESS 2H minimum
GLOSS LEVEL (60°) 80-95+
SALT SPRAY 1,000 hours
BALL IMPACT 80 in/lb
SDS Sheet info # #9 – Polyester TGIC Metallic
SDS link https://emeraldcoatings.com/sds-sheets/
*Clear Coat Recommended, will Improved Mar Resistance and will improve the over all look and depth of the metallic finish.  *When coating in 2-3 stages, always particularly cure the base coat around 50-75% of the recommended cure schedule to allow the top coat to properly cross-link with the base coat. This method of curing will result in the best possible bond between coats. Over curing the base coat can cause possible delamination between coatings.
Comments Off on FLAME RED COPPER BLAST

TOXIC WASTE GREEN

Posted on July 16, 2013 by Adam Robertson
MC1078 TOXIC WASTE GREEN
CHEMISTRY Polyester TGIC Metallic
REGULAR CURE TEMP 375F/10 MIN
MIN TEMP 350F/15 MIN
MAX TEMP 400F/7 MIN
RECOMMENDED THICKNESS 2.5 TO 4 MILS
PENCIL HARDNESS 2H
SPECIFIC GRAVITY 1.38 +/- .05
THEORETICAL COVERAGE 56 sq/ft @ 2.5 mils
PENCIL HARDNESS 2H minimum
GLOSS LEVEL (60°) 80-95+
SALT SPRAY 1,000 hours
BALL IMPACT 120 in/lb
SDS Sheet info # #9 – Polyester TGIC Metallic
SDS link https://emeraldcoatings.com/sds-sheets/
*Clear Coat Recommended, will Improved Mar Resistance and will improve the over all look and depth of the metallic finish.  *When coating in 2-3 stages, always particularly cure the base coat around 50-75% of the recommended cure schedule to allow the top coat to properly cross-link with the base coat. This method of curing will result in the best possible bond between coats. Over curing the base coat can cause possible delamination between coatings.

 

 

 

Comments Off on TOXIC WASTE GREEN